Free Practice Questions for API API-571 Exam

According to API RP 571 and API RP 751 (HF Alkylation Units):

“HF acid corrosion rates increase with elevated temperature and higher water content. This is because water acts as an ionizing agent that facilitates the acid’s attack on steel.”

“Corrosion is minimized when water content is strictly controlled, usually between 0.5–1.5%.”

“Contrary to some assumptions, increasing HF acid concentration actually decreases corrosivity.”

Hence, option B is correct.

Same as above. Sigma phase formation is a microstructural phenomenon and not typically detected by NDE methods like magnetic particle or surface hardness testing.

Therefore, metallographic testing remains the definitive detection method, confirming option D again as the correct answer.

According to API RP 571 and API RP 751:

“In HF alkylation units, carbon steel can be used if weld hardness is controlled to ≤ 200 Brinell (BHN). Exceeding this can significantly increase the corrosion rate and susceptibility to cracking.”

“Hard welds act as preferential corrosion sites due to microstructural inhomogeneity and stress concentration.”

(Reference: API RP 571, Section 4.3.3.4 – Hydrofluoric Acid Corrosion; API RP 751, Section 5.3 – Materials of Construction)

Thus, option D is correct.

API RP 571 under Atmospheric Corrosion notes:

“The highest corrosion rates are typically observed between 80°F and 120°F (27°C–49°C), particularly when relative humidity is high and surfaces are wet from condensation or rain.”

“At higher temperatures, surface dryness generally reduces corrosion activity despite increased reaction kinetics.”

(Reference: API RP 571, Section 4.3.1.3 – Atmospheric Corrosion)

Thus, among the listed temperatures, 175°F is closest to the upper end of the most active corrosion window, making option A the most accurate answer.