Free Practice Questions for API API-571 Exam

According to API RP 571, under the section "Corrosion in Aqueous Environments – Cooling Water Corrosion", one of the key contributors to corrosion in carbon steel and other materials used in heat exchangers is the presence of dissolved oxygen. API RP 571 states:

"Oxygen is a primary contributor to corrosion in cooling water systems. Systems open to the atmosphere are typically more corrosive than closed systems due to the continual replenishment of oxygen."

"Corrosion rates are highest where oxygen concentration is the greatest, especially in systems using untreated or poorly treated water."

"Carbon steel corrodes in the presence of oxygen and water, forming corrosion products that may or may not adhere to the surface."

(Reference: API RP 571, Section 4.3.1.1 – Cooling Water Corrosion)

Therefore, increasing oxygen content directly increases corrosion activity in exchanger tubes, making option C the correct and documented answer.

Comprehensive and Detailed Explanation From Exact Extract:

According to API RP 571, amine stress corrosion cracking (Amine SCC) is a form of environmentally assisted cracking that occurs in alkanolamine systems (e.g., MEA, DEA, DGA) used for acid gas treating. The cracking mechanism requires the simultaneous presence of tensile stress, susceptible microstructure, and an amine environment.

API RP 571 clearly states that Amine SCC occurs primarily in the weld heat affected zone (HAZ) of carbon and low-alloy steels. The reasons include:

The HAZ contains high residual stresses from welding.

The microstructure in the HAZ is metallurgically altered, making it more susceptible than base metal.

Cracks often initiate adjacent to welds, not in the weld metal itself.

Why the other options are incorrect:

Option A (Weld fusion line) is not the primary cracking location.

Option C (Weld metal) generally has different chemistry and lower susceptibility.

Option D (Base metal) typically has lower residual stress and is less prone.

API RP 571 specifically identifies the weld HAZ as the dominant cracking location for Amine SCC.

Referenced Documents (Study Basis):

API RP 571 – Section on Amine Stress Corrosion Cracking

API Corrosion and Materials Study Guide

======================

API RP 945, dedicated to environmental cracking in amine units, states:

“Carbon steel is widely used in amine systems but is particularly susceptible to localized corrosion, under-deposit corrosion, and stress corrosion cracking, especially in high-pressure or rich amine environments.”

“Proper control of amine quality, oxygen ingress, and temperature is critical to avoid accelerated corrosion in carbon steel equipment.”

Thus, carbon steels are the most commonly affected materials, making option C correct.

As per API RP 571 Section 5.3.2.2 (Sigma Phase Embrittlement):

“Sigma phase embrittlement occurs in austenitic stainless steels (like 300 series) and duplex stainless steels exposed to 1000°F to 1800°F (540°C to 980°C)... This embrittlement results in a significant loss of toughness and ductility.”

Sigma phase is not a concern in Monel (nickel-copper alloy) or 5Cr steels.

400 series are ferritic and not typically affected by sigma phase.

Hence, Option A (300 series stainless steel) is correct.

API RP 571 states in the section on Creep Damage:

“Creep damage in carbon steels generally becomes a concern above 700°F (371°C), especially for steels with higher tensile strength (greater than 60 ksi).”

“For prolonged exposure above this temperature, time-dependent deformation can lead to material degradation and cracking, especially at weldments and stress concentrations.”

Thus, the lowest threshold for creep in high-strength carbon steels is 700°F (371°C), making option B correct.

According to API RP 571, under Caustic Stress Corrosion Cracking (Caustic Embrittlement):

“Cracking occurs in stressed components exposed to caustic (e.g., sodium hydroxide).”

“The most effective mitigation strategy is postweld heat treatment (PWHT), which relieves residual stress that promotes cracking.”

“Upgrading materials or controlling concentration may help, but do not replace stress relief.”

(Reference: API RP 571, Section 4.2.2.3 – Caustic SCC)

Thus, PWHT is the most effective prevention technique, making option A correct.

As per API RP 571 on Sigma Phase Embrittlement:

“Sigma phase embrittlement occurs in stainless steels and nickel-based alloys due to the formation of a brittle intermetallic phase in the temperature range of 1050°F to 1650°F (565°C to 900°C).”

“This damage mechanism is not easily detected through surface or hardness testing and typically requires metallographic examination to confirm the presence of sigma phase in the microstructure.”

Metallographic testing allows clear identification of sigma phase particles and is thus the most reliable method, making option D correct.

Comprehensive and Detailed Explanation From Exact Extract:

In HF Alkylation units, API RP 571 identifies certain residual alloying elements in carbon steel that can significantly increase corrosion rates in HF acid service.

The most detrimental residual elements are:

Chromium (Cr)

Copper (Cu)

Nickel (Ni)

These elements:

Disrupt formation of protective iron fluoride films

Increase general and localized corrosion rates

Are tightly controlled in carbon steel specifications for HF service

Referenced Documents (Study Basis):

API RP 571 – Section on Hydrofluoric Acid Corrosion

======================

Hydrogen Stress Cracking (HSC) is a subclass of environmental cracking that occurs in certain materials when hydrogen is present. According to API RP 571, HSC typically affects high-strength low alloy steels and carbon steels, particularly under tensile stress in a hydrogen-containing environment. This includes areas like weld-affected zones and hard spots in steels.

From API RP 571 Section 5.1.2.1 (Hydrogen-Induced Cracking):

"Hydrogen stress cracking (HSC) can occur in carbon steel and low alloy steels in environments containing hydrogen at ambient to moderately elevated temperatures (up to 200°F or 93°C)... Hardness is a critical factor for HSC. High hardness in welds and heat affected zones (HAZ) are most susceptible."

Additionally, API RP 939-C does not directly define HSC but reinforces the relationship between hydrogen exposure and metal integrity, particularly under conditions not exceeding 450 °F (230 °C) for hydrogen services.

Thus, option A is correct, as it directly reflects the metal types most susceptible to HSC in operational environments defined by API RP 571.

According to API RP 571 and API RP 583:

“The most effective mitigation of CUI is the use of appropriate coatings underneath the insulation, which are resistant to moisture and chloride ingress.”

“Inspection and insulation selection are also important but are secondary controls.”

(Reference: API RP 571, Section 4.3.4 – Corrosion Under Insulation; API RP 583)

Hence, option D is correct.